Physicochemical and biological characterization of Ti6Al4V particles obtained by implantoplasty: an in vitro study. Part I
Autor/a
Toledano-Serrabona, Jorge
Gil Mur, Francisco Javier
Camps Font, Octavi
Valmaseda-Castellon, Eduard
Gay Escoda, Cosme
Sánchez-Garcés, M. Angeles
Data de publicació
2021ISSN
1996-1944
Resum
Implantoplasty is a mechanical decontamination technique that consists of polishing the supra-osseous component of the dental implant with peri-implantitis. This technique releases metal particles in the form of metal swarf and dust into the peri-implant environment. In the present in vitro study, the following physicochemical characterization tests were carried out: specific surface area, granulometry, contact angle, crystalline structure, morphology, and ion release. Besides, cytotoxicity was in turn evaluated by determining the fibroblastic and osteoblastic cell viability. As a result, the metal debris obtained by implantoplasty presented an equivalent diameter value of 159 µm (range 6–1850 µm) and a specific surface area of 0.3 m2/g on average. The particle had a plate-like shape of different sizes. The release of vanadium ions in Hank’s solution at 37 °C showed no signs of stabilization and was greater than that of titanium and aluminum ions, which means that the alloy suffers from a degradation. The particles exhibited cytotoxic effects upon human osteoblastic and fibroblastic cells in the whole extract. In conclusion, metal debris released by implantoplasty showed different sizes, surface structures and shapes. Vanadium ion levels were higher than that those of the other metal ions, and cell viability assays showed that these particles produce a significant loss of cytocompatibility on osteoblasts and fibroblasts, which means that the main cells of the peri-implant tissues might be injured.
Tipus de document
Article
Versió del document
Versió publicada
Llengua
English
Matèries (CDU)
616.3 - Patologia de l'aparell digestiu. Odontologia
Paraules clau
Implant dental
Periimplantitis
Aliatge de titani
Implantoplàstia
Implante dental
Periimplantitis
Aleación de titanio
Implantoplastia
Dental implant
Peri-implantitis
Titanium alloy
Implantoplasty
Pàgines
13
Publicat per
MDPI
Col·lecció
14; 21
Publicat a
Materials
Citació
Toledano-Serrabona, Jorge; Gil-Mur, Francisco Javier; Camps-Font, Octavi [et al.]. Physicochemical and biological characterization of Ti6Al4V particles obtained by implantoplasty: an in vitro study. Part I. Materials, 2021, 14(21), 6507. Disponible en: <https://www.mdpi.com/1996-1944/14/21/6507>. Fecha de acceso: 23 nov. 2021. DOI: 10.3390/ma14216507
Número de l'acord de la subvenció
info:eu-repo/grantAgreement/MICINN/RTI2018-098075-B-C21
info:eu-repo/grantAgreement/MICINN/RTI2018-098075-BC22
Aquest element apareix en la col·lecció o col·leccions següent(s)
- Odontologia [245]
Drets
This is an open access article distributed under the Creative Commons Attribution License which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Excepte que s'indiqui una altra cosa, la llicència de l'ítem es descriu com https://creativecommons.org/licenses/by/4.0/